The following table contains some
numbers found in the literature. It is not complete, eventually it might get
"fuller". |
|
|
|
|
|
Schottky Disorder
Crystal |
HF
[eV] |
SF
[k] |
HM Cation vacancy
[eV] |
HM Anion
vacancy
[eV] |
LiF |
2.5 1)
2.342), 3) |
9.61) |
0.71) |
0.71) |
LiCl |
2.122), 3) |
|
|
|
LiBr |
1.83) |
|
|
|
LiI |
1,33) |
|
|
|
NaCl |
2.31), 2), 3) |
61) |
0.71) |
1.01) |
KCl |
2.31)
2.263) |
6.51) |
0.71) |
1.01) |
KBr |
2.41) |
8.61) |
0.61) |
0.91) |
CsI |
1.91) |
- |
0.61) |
0.31) |
MgO |
6.62) |
|
|
|
CaO |
6.1 |
|
|
|
|
|
|
|
|
|
|
|
|
Frenkel
Disorder
|
HF
[eV] |
SF
[k] |
Hm Anion
interstitial
[eV] |
HM Anion vacancy
[eV] |
AgCl |
1.62), 3) |
|
|
|
AgBr |
1,203) |
|
|
|
β - AgI |
0,73) |
|
|
|
CaF2 |
2.71)
2.82), 3) |
- |
»
1.01) |
0.61) |
SrF2 |
2.31)
0.73) |
- |
0.81) |
0.91) |
BaF2 |
1.91) |
- |
0.71) |
0.61) |
PbF2 |
1.11) |
- |
- |
- |
SrCl2 |
1.71) |
- |
- |
- |
ZrO2 |
4.12) |
|
|
|
UO2 |
3.42) |
|
|
|
|
|
|
|
|
|
1) From "Hayes and Stoneham"; Defects an Defect
Processes in Nonmetallic Solids |
|
|
2)
From
University of Hull, Lectures |
|
|
3)
From Uni
Lethbridge; California. |
© H. Föll